duracote FT (Fine Texture) an approved protection and waterproof coating

All surfaces which are to receive the coating must be free from oil, grease, wax, dirt or any other form of foreign matter that might affect adhesion. Typically, concrete may require grit blasting.

Spalled surfaces or those containing large blowholes and other such defects should be repaired using or an a.b.e.^® approved repair mortar. Care must be taken when choosing the repair mortar to ensure that it has all necessary approvals for contact with potable water. If the surface contains small blowholes, typically less than 1 mm wide, the coating can be applied directly onto the substrate without the need for a treatment. Cracks which
are less than 0.3 mm in width can be overcoated as long as the crack is not likely to open up to greater than 0.3 mm (this is greater than the maximum permissible crack widths recommended in BS 8007: 1987, the British Standard Code of Practice for the design of concrete structures for retaining aqueous liquids).

Cracks which are greater than 0.3 mm in width should be chased-out to 4 mm in width and approximately 15 mm in depth. This should be filled with duracote FT (applied using less liquid provides a thicker consistency). When the material in the crack has hardened, the coating should be applied over the crack.

Self-priming.

The liquid component should be poured into a plastic or metal drum having a volume of at least 20 litres. This should be placed onto a plastic sheet to avoid contamination. The powder component is gradually added to the liquid whilst mixing with a Paddle Mixer or other approved spiral paddle attachment on a variable speed drill.

Mixing is continued, constantly moving the paddle around the drum, until a lump-free slurry is obtained. This should take a minimum of 3 minutes and a maximum of 5 minutes.
Note:  The preferred drill speed is between 280 and 640 r/min.

MIXING WARNING
duracote FT may exhibit satisfactory handling characteristics even though inadequately mixed. This will result in a significantly lower level of performance or possible failure. It is therefore essential that mixing instructions are strictly adhered to with particular emphasis on the time of the mixing operation.

Typical coverage rate: 8 m²/15 kg for 1 mm wet film thickness. The coverage figure given is theoretical due to wastage factors and the variety and nature of possible substrates, practical coverage figures will be reduced. A minimum coverage of 2 kg/m²/mm applied in not less than two coats is recommended.

Pre-wetting of substrate
Thoroughly dampen the substrate surface with water using a brush, roller, or spray bottle. High porosity substrates will require more dampening than dense substrates. Do not apply the coating when the substrate is wet, but allow the water to soak in until the substrate is just visibly damp before proceeding. Any excess water should be removed using a sponge.
Any running water should be stopped with a suitably approved plugging mortar such as durarep 60. Contact the local a.b.e.^®  office for further advice on suitable materials.
General
The first coat should be applied at a wet film thickness of 1 mm (coverage per coat is 1.8 kg/m²). To ensure the correct thickness is achieved, measure out an area (for example 200 m²), then calculate how much material will be needed to cover this area. Monitor the coating thickness during application at regular intervals using a wet film gauge. Care must be taken
to attempt to fill all imperfections such as blowholes during application. If not, they can be filled while the coating is still fluid by using a dry sponge. If the coating has dried before these imperfections are found, they can be filled using fresh material. Allow first coat to cure for a minimum of 4 hours at 20 °C/50% RH and longer at lower temperatures or higher
humidity. The exact drying time will depend on surface temperature, relative humidity, and air movement. High temperatures and/or low humidity will reduce the drying time. This can vary from 1 – 16 hours. The maximum ambient temperature for application is 40 °C. The first coat should be left to dry until firm and unmarkable to the touch. There is no maximum time between coats, however the surface may need cleaning with water prior to application of the second coat. No curing membrane is necessary; however, the freshly applied coating should be protected from rain. No curing membrane is necessary.
Brush application
The most suitable type of brush is a soft-bristled wallpaper paste brush (120 to 220 mm wide). Where larger areas are to be applied it is advisable to use a brush with a handle. Load the brush up well and spread the material to the required thickness. If the brush begins to drag during application, do not add water to the material but dampen the surface again. Finish in one direction for a neat appearance. For floor application, a soft-bristled broom is recommended. Pour the material onto the substrate and then spread to the required thickness.
Roller Application
Application by roller has the benefit of speed over brush application, particularly on smooth substrates. A good quality medium hair roller is recommended. The roller should be well loaded for ease of application. A heavy roller pattern will be left; therefore, it is important to use a finishing tool to produce a smooth coating with a uniform 1 mm wet film thickness.
Finishing Tools
A finishing tool may be required to produce a smooth finish or to repair film defects. Examples of suitable tools include a steel plastering trowel, a caulking tool, and a hand sponge. All of these must be used immediately after coating application, otherwise the coating may drag or tear. When using a hard sponge, it should be dry or very slightly damp. A
wet sponge should not be used as this will cause polymer to come to the surface of the coating which causes an unsightly white streaky effect.

Note: should a reinforcing membrane be used in conjunction with the duracote FT ensure that it is ecofelt as it is alkali resistant.

Sealed joints
Sealant joints should be filled with a suitable joint sealant before application of duracote FT. If potable water contact is expected, the sealant should be approved. Contact your local a.b.e.^®  office for recommendations.

Immediately after application is completed, clean all tools and equipment with clean water. Hardened material can be removed by mechanical means. Waste material should be allowed to harden overnight then disposed of as non-hazardous waste.

Allow a minimum cure time of equivalent to 7 days at 7 °C (3 days at 20 °C and above). This is to ensure the full physical properties are developed.

duracote FT should not be used when the temperature is below 5 °C. The product should not be exposed to rainfall or moving water during application or within 4 hours at 20 °C. The maximum ambient temperature for application is 40 °C. duracote FT should not be used on external surfaces where an aesthetic appearance is critical because differences in environmental conditions during cure may cause colour differences in the final surface. If any doubts arise concerning temperature or substrate conditions, consult the local a.b.e.^® office.

See “Properties of mixed material”.

The waterproofing coating is duracote FT, an elastomeric cementitious coating approved under the UK Water Bylaws Scheme (WRC listed). Two component polymer modified cementitious anticarbonation and chloride ion barrier coating and waterproofing coating. The barrier coating shall be duracote FT, a two component, polymer modified, cementitious compound applied in accordance with the manufacturer’s recommendations, a.b.e.® The coating shall provide a waterproof, anti-carbonation, and chloride ion barrier. The compound shall have a resistance in excess of 10 bar positive water pressure and 4 bar negative pressure.

duracote FT is supplied in 15 kg cartons containing 10.2 kg grey and white powder in polyethylene bags and 4.8 kg liquid polymer in plastic container.

This product has a shelf life of 6 months if kept in a dry cool place in the original packaging. In more extreme conditions this period might be shortened. The liquid component must not be allowed to freeze.

duracote FT powder is irritating to eyes, respiratory system, and skin. Avoid inhalation of dust and wear suitable respiratory protectivevequipment. duracote FT liquid is not classified as dangerous. duracote FT when mixed becomes highly alkaline. Wear suitable
protective clothing, gloves and eye protection. For both components and mixed material, avoid contact with skin and eyes. In case of contact with eyes or skin rinse immediately with plenty of water and seek medical advice.

This data sheet is issued as a guide to the use of the product(s) concerned. Whilst a.b.e.^® endeavours to ensure that any advice, recommendation, specification, or information is accurate and correct, the company cannot – because a.b.e.^® has no direct or continuous control over where and how a.b.e.^® products are applied – accept any liability either directly or indirectly arising from the use of a.b.e.^® products, whether or not in accordance with any advice, specification, recommendation, or information given by the company.

Where other products are to be used in conjunction with this material, the relevant technical data sheets should be consulted to determine total requirements. a.b.e.^® has a wealth of technical and practical experience built up over years in the company’s pursuit of excellence in building and construction technology.